Section |
Dimensions |
Mass |
Moment of inertia |
Modulus of Section |
|||
|
Width |
Height |
Thickness |
Per pile |
Wall |
|
|
|
|
w |
h |
t |
|
|
|
|
|
|
mm |
mm |
mm |
kg/m |
kg/m2 |
cm3/m |
cm4/m |
|
|
OZ 13A |
675 |
399 |
6.5 |
55.5 |
82.2 |
1,370 |
27,251 |
|
OZ 14A |
675 |
399 |
7 |
59.7 |
88.5 |
1,470 |
29,281 |
|
OZ 15A |
675 |
400 |
7.5 |
64 |
94.8 |
1,570 |
31,325 |
|
OZ 16A |
675 |
400 |
8 |
68.2 |
101.1 |
1,670 |
33,350 |
|
OZ 17A |
685 |
401 |
8.5 |
72.3 |
105.6 |
1,780 |
35,558 |
|
OZ 18A |
685 |
401 |
9 |
76.6 |
111.8 |
1,880 |
37,580 |
|
OZ 19A |
685 |
402 |
9.5 |
80.8 |
118.0 |
1,970 |
39,595 |
|
OZ 20 |
650 |
437 |
8 |
70.8 |
108.9 |
1,980 |
43,290 |
|
OZ 20A |
685 |
402 |
10 |
85.1 |
124.2 |
2,070 |
41,601 |
|
OZ 21 |
650 |
438 |
8.5 |
75.1 |
115.5 |
2,100 |
45,910 |
|
OZ 22 |
650 |
438 |
9 |
79.4 |
122.2 |
2,220 |
48,520 |
|
OZ 23A |
650 |
439 |
9.5 |
83.6 |
128.6 |
2,330 |
51,120 |
|
OZ 24A |
650 |
439 |
10 |
87.9 |
135.2 |
2,450 |
53,710 |
|
OZ 25A |
650 |
440 |
10.5 |
92.3 |
142 |
2,560 |
56,387 |
|
OZ 26 |
675 |
440 |
10.5 |
95.9 |
142.1 |
2,620 |
57,410 |
|
OZ 27 |
675 |
440 |
11 |
99.8 |
147.9 |
2,730 |
60,043 |
|
OZ 28A |
675 |
441 |
11.5 |
104.4 |
154.6 |
2,850 |
62,667 |
|
OZ 29A |
675 |
441 |
12 |
108.9 |
161.3 |
2,960 |
65,281 |
|
OZ 31A |
675 |
442 |
12.7 |
115.2 |
170.7 |
3,120 |
68,927 |
|
OZ 32 |
675 |
487 |
11 |
108.3 |
160.4 |
3,180 |
77,370 |
|
OZ 33 |
675 |
488 |
11.5 |
113.1 |
167.6 |
3,320 |
80,750 |
|
OZ 34A |
675 |
488 |
12 |
117.8 |
174.5 |
3,450 |
84,120 |
|
OZ 36 |
675 |
489 |
12.5 |
122.5 |
181.5 |
3,580 |
87,470 |
|
OZ 37 |
675 |
489 |
13 |
127.3 |
188.6 |
3,720 |
90,830 |
|
OZ 38A |
675 |
490 |
13.5 |
132 |
195.6 |
3,850 |
94,170 |
|
OZ 40 |
675 |
490 |
14 |
136.6 |
202.4 |
3,980 |
97,490 |
|
OZ 40-700 |
700 |
600 |
11 |
117.2 |
167.4 |
4,000 |
120,087 |
|
OZ 41A-700 |
700 |
600 |
11.5 |
122.5 |
175 |
4,170 |
125,137 |
|
OZ 43-700 |
700 |
600 |
12 |
127.8 |
182.6 |
4,340 |
130,151 |
|
OZ 45-700 |
700 |
600 |
12.5 |
133.2 |
190.2 |
4,500 |
135,130 |
|
OZ 46A-700 |
700 |
600 |
13 |
138.5 |
197.8 |
4,670 |
140,075 |
|
OZ 48-700 |
700 |
600 |
13.5 |
143.8 |
205.4 |
4,830 |
144,986 |
|
OZ 50-700 |
700 |
600 |
14 |
149.1 |
213 |
5,000 |
149,862 |
|
OZ 50A-700 |
700 |
600 |
14.2 |
151.3 |
216.1 |
5,070 |
151,970 |
|
OZ 51-700 |
700 |
600 |
14.3 |
152.3 |
217.6 |
5,100 |
153,024 |
|
OZ 51A-700 |
700 |
600 |
14.5 |
154.5 |
220.7 |
5,170 |
155,135 |
|
OZ 27W-750 |
750 |
560 |
10 |
96.9 |
129.3 |
2,719 |
76,138 |
|
OZ 28W-750 |
750 |
560 |
10.5 |
101.6 |
135.4 |
2,845 |
79,672 |
|
OZ 29AW-750 |
750 |
560 |
11 |
106.4 |
141.9 |
2,956 |
82,782 |
|
OZ 31W-750 |
750 |
560 |
11.5 |
111.3 |
148.3 |
3,087 |
86,428 |
|
OZ 32W-750 |
750 |
560 |
12 |
116.1 |
154.8 |
3,205 |
89,734 |
|
OZ 33W-750 |
750 |
560 |
12.5 |
120.9 |
161.2 |
3,335 |
93,383 |
|
OZ 33AW-750 |
750 |
560 |
12.7 |
122.9 |
163.8 |
3,384 |
94,739 |
|
OZ 34AW-750 |
750 |
560 |
13 |
125.8 |
167.7 |
3,455 |
96,733 |
|
OZ 35AW-750 |
750 |
560 |
13.5 |
130.6 |
174.1 |
3,575 |
100,095 |
|
OZ 37W-750 |
750 |
560 |
14 |
135.4 |
180.6 |
3,693 |
103,407 |
OZ Palplanche Chacun de ces processus OZ43-700 OZ45-700 se produit davantage à certaines étapes OZ46A-700 du parcours d'une rivière OZ48-700 et moins OZ50-700, pendant d'autres parties de son parcours OZ50A-700. Lorsque l'humidité OZ43-700 est éliminée du sable vert OZ 43-700, il est connu sous le nom de sable sec. La fracture d'un solide se produit généralement en raison du développement de certaines surfaces de discontinuité de déplacement au sein du solide.
Profils Z Palplanches Profilées à Froid Le verre OZ 50-700 est composé de silicate de sodium OZ 43-700 et de silicate de calcium OZ 45-700 OZ 50A-700, il est donc également appelé OZ 46A-700 comme verre sodocalcique OZ 48-700. L'adhérence est la propriété du sable OZ50A-700 grâce à laquelle les particules de sable collent aux parois de la boîte de moulage. Les rivières naissent aux points hauts des collines ou des montagnes et sont ensuite rejointes par d'autres ruisseaux et rivières aux confluences.
La pliabilité est la propriété du sable OZ48-700 grâce à laquelle le moule en sable OZ 50-700 s'effondre automatiquement après la solidification de la pièce moulée. Les blocs de verre OZ 45-700 ou les briques de verre sont fabriqués à partir de deux moitiés différentes OZ 50A-700 et elles sont pressées et recuites ensemble OZ 46A-700 pendant le processus de fusion du verre. Bien que l'OZ46A-700 puisse paraître très lent et calme à sa surface, il a toujours une grande puissance OZ 48-700 et continue de transporter les sédiments.
+86-18018031808 
+86-18018031808